Ultrasonic Detection of Manufacturing Artifacts in New Pipe

Automatic Fastener Hole inspection in Aircraft


Detection of internal wall reduction artifacts in manufactured pipe.


Localized wall reductions are not always caused by corrosion. Wall reductions can develop during plate rolling or the initial stages of forming in the pipe manufacturing process. Impressions in the steel can be created by the forming rollers. High surface pressure and heat applied to the forming rollers can induce spalling. Metal pieces that spall and become detached from the rollers can fall into the path of the incoming plate causing the pieces to bond to the roller. Once the pieces are bound to the roller, impressions begin occurring in the plate being rolled. Hence the term artifacts from the impression caused by the roller, which appear similar to be wall reductions caused by corrosion.

In many cases new pipe is put into service with such artifacts. When corrosion inspection is later performed after he pipe has been in operation, inspectors may find these wall reduction artifacts and mistake them for corrosion cells. If this occurs, process engineers may infer an incorrectly fast corrosion rate and make incorrect process changes and or chemical additives. However a simple ultrasonic gaging procedure can identify artifacts at the manufacturing or installation stage.


Model 38DLP PLUS thickness gage, or Model 45MG gage with waveform display option, and D790 dual element transducer (5 MHz).


The pipe in the picture below is 8” x .250” wall carbon steel 1018 grade manufactured with the ERW process. The dark indentions are artifacts reducing wall thickness that occurred during the pipe forming process. No corrosion was present on the ID or OD.

The pipe in the picture below is 8” x .250” wall carbon steel 1018 grade manufactured with the ERW process

Thickness gaging is performed in the same manner as a corrosion survey. In the picture at left, the gage is reading full wall thickness. In the picture at right, the thinner reading indicates a wall thinning artifact on the inside surface.

The gage is reading full wall thickness
The thinner reading indicates a wall thinning artifact on the inside surface.

An inspector may consider the following factors when attempting to distinguish manufacturing artifacts from corrosion cells:

  • Determine if the pipe is ERW or seamless.
  • Identify that the wall reductions are oriented in an axial line rather than randomly.
  • If multiple or all joints are ERW in the piping circuit, determine the line where the artifacts are located on each joint. The inspector may find that the line changes azimuth position as relative to the piping.
  • If a joint of pipe in the circuit is found to be seamless and there are no wall reductions.


Manufacturing artifacts in pipe can be detected by ultrasonic thickness gaging. Inspectors performing thickness measurement of piping should be aware of this damage mechanism. It is also important to inform the process plant quality control inspectors of this potential problem to avoid over-estimating corrosion rates.

Olympus IMS

Das 45MG ist ein Ultraschalldickenmesser mit Standardmessfunktionen und optionalen Softwarefunktionen. Dieses einzigartige Gerät ist mit der gesamten Palette von Olympus Einzelschwinger- und Sender-Empfängermessköpfen kompatibel, was dieses innovative Gerät zu einer Universallösung für nahezu jeden Anwendungsbereich in der Dickenmessung macht.
Das 38DL PLUS ist ein hochentwickelter Ultraschalldickenmesser. Es misst mit Sender-Empfängerschallkopf Korrosionen im Inneren von z. B. Rohren und besitzt eine THRU-COAT und Echo-Echo-Funktion. Es misst mit Einschwingermessköpfen dünne, sehr dicke oder mehrschichtige Werkstoffe sehr genau.
Sorry, this page is not available in your country
Let us know what you're looking for by filling out the form below.

Diese Seite verwendet Cookies, um die Leistung zu verbessern, Datenverkehr zu analysieren und Werbeanzeigen zu personalisieren. Wenn Sie Ihre Browser-Einstellungen nicht ändern, werden weiterhin Cookies auf dieser Webseite verwendet. Um zu erfahren wie Cookies auf dieser Webseite verwendet werden und wie Sie unsere Verwendung von Cookies beschränken, lesen Sie unsere Cookie-Richtlinie.