Corrosion Gaging with Dual Element Transducers

Application:

The use of dual element transducers (“duals”) to measure remaining metal thickness in corrosion applications.

Problem:

Just about anything that is made of common structural metals can be subject to corrosion. A particularly important problem that many industries face is the measurement of remaining wall thickness in pipes, tubes, or tanks that may be corroded on the inside surface. Such corrosion is often not detectable by visual inspection without cutting or disassembling the pipe or tank. Structural steel beams, particularly bridge supports and steel pilings, are also subject to corrosion that reduces the original thickness of the metal. If undetected over a period of time, corrosion will weaken walls and possibly lead to dangerous structural failures. Both safety and economic considerations require that metal pipes, tanks, or structures that are subject to corrosion be inspected on a regular basis. Ultrasonic testing is a widely accepted nondestructive method for performing this inspection, and ultrasonic testing of corroded metal is usually done with dual element transducers.

Theory Of Operation:

The irregular surfaces that are frequently encountered in corrosion situations give duals an advantage over single element transducers. All ultrasonic gaging involves timing the round trip of a sound pulse in a test material. Because solid metal has an acoustic impedance that differs from that of gasses, liquids, or corrosion products, such as scale or rust, the sound pulse will reflect from the far surface of the remaining metal. The test instrument is programmed with the velocity of sound in the test material, and computes the wall thickness from the simple formula Distance = (Velocity) × (Time).

Most gages designed for corrosion applications measure the round trip transit time interval to the first backwall echo. Many instruments can also measure the interval between successive multiple echoes. This technique can be very useful in situations involving thick paint or similar coatings, however echo-to-echo measurement can be less effective at detecting pitting and measuring the true minimum thickness of pitted pipe or tank walls.

Dual element transducers incorporate separate transmitting and receiving elements mounted on delay lines that are usually cut at an angle to the horizontal plane (the roof angle) so that the transmitting and receiving beam paths cross beneath the surface of the test piece. This crossed-beam design of duals provides a pseduo-focusing effect that optimizes measurement of minimum wall thickness in corrosion applications. Duals will typically be more sensitive than single element transducers to echoes from the base of pits that represent minimum remaining wall thickness. Also, duals may often be used more effectively on rough outside surfaces. Couplant trapped in pockets on rough sound entry surfaces can produce long, ringing interface echoes that interfere with the near-surface resolution of single element transducers. With a dual, the receiver element is unlikely to pick up this false echo. Finally, duals may be designed for high-temperature measurements that would damage single element contact transducers.

Equipment:

A number of small, handheld ultrasonic thickness gages have been specifically designed for corrosion survey applications. Typically, these gages will be used with a dedicated group of dual element transducers, covering various thickness ranges and temperature conditions. In some critical applications, especially at elevated temperatures, a user may require an ultrasonic waveform display to help verify that valid echoes are being detected. The 38DL PLUS® thickness gage has a waveform display that is designed for such cases. For full details, see the instrument’s datasheet. Another instrument designed for this type of testing is the 45MG thickness gage. In corrosion applications, duals can be used effectively with flaw detectors as well. Digital flaw detectors, such as the Olympus EPOCH® series (EPOCH 650, and EPOCH 6LT) provide a thickness measurement as well as a waveform display.

Procedure:

The following general principles apply to all corrosion measurements with dual element transducers, whether used with a portable thickness gage, or with a flaw detector. Keep in mind that, in all cases, the instrument must be properly calibrated for sound velocity and zero offset in accordance with the procedure found in the instrument’s operating manual.

1. Transducer Selection:

For any ultrasonic measurement system (transducer plus thickness gage or flaw detector) there will be a minimum material thickness below which valid measurements will not be possible. Normally, this minimum range will be specified in the manufacturer’s literature. As transducer frequency increases, the minimum measurable thickness decreases. In corrosion applications, where minimum remaining wall thickness is normally the parameter being measured, it is particularly important to be aware of the specified range of the transducer being used. If a dual is used to measure a test piece that is below its designed minimum range, the gage may detect invalid echoes and display an incorrectly high thickness reading. The table below lists approximate minimum measurable thicknesses in steel for the standard transducers used with the 38DL PLUS and 45MG gages. Note that these numbers are approximate. The exact measurable minimum in a given application depends on material velocity, surface condition, and geometry, and it should be determined experimentally by the user.

Transducer

Diameter

Freq.

Connector

Approx. Minimum Thickness

Approx. Minimum Radius

Temp. Limit*

In.

mm

MHz

In.

mm

In.

mm

°F

°C

D790, D790-SM

0.434

11

5

Straight

0.04

1

0.75

20

-5 to 932

-20 to 500

D791

0.434

11

5

Right Angle

0.04

1

0.75

20

-5 to 932

-20 to 500

D791-RM

0.434

11

5

Right Angle

0.04

1

0.75

20

-5 to 752

-20 to 400

D7912

0.295

7.5

10

Straight

0.02

0.5

0.50

12.7

32 to 122

0 to 50

D7913

0.295

7.5

10

Right Angle

0.02

0.5

0.50

12.7

32 to 122

0 to 50

D794

0.283

7.2

5

Straight

0.03

0.75

0.50

12.7

32 to 122

0 to 50

D797-SM

0.900

22.9

Straight

0.15

3.8

4.00

100

-5 to 752

-20 to 400

D797

0.900

22.9

2

Right Angle

0.15

3.8

4.00

100

-5 to 752

-20 to 400

D798

0.282

7.2

7.5

Right Angle

0.02

0.71

0.50

12.7

-5 to 300

-20 to 150

D799

0.434

11

5

Right Angle

0.04

1

0.75

20

-5 to 300

-20 to 150

D7226

0.350

8.9

7.5

Right Angle

0.02

0.71

0.50

12.7

-5 to 300

-20 to 150

D7906-SM

0.434

11

5

Straight

0.04

1

0.75

20

32 to 122

0 to 50

D7906-RM

0.434

11

5

Straight

0.04

1

0.75

20

32 to 122

0 to 50

D7908

0.283

2

7.5

Straight

0.04

1

0.50

12.7

32 to 122

0 to 50

D7910

0.500

7

5

Right Angle

0.04

1

1.00

25

32 to 122

0 to 50

MTD705

0.200

5.1

5

Right Angle

0.04

1

0.50

12.7

32 to 122

0 to 50

*Gain adjustments may be needed to make accurate measurements on radiuses at or below specified minimum

2. Surface Condition:

Loose or flaking scale, rust, corrosion, or dirt on the outside surface of a test piece will interfere with the coupling of sound energy from the transducer into the test material. Thus, any loose debris of this sort should be cleaned from the specimen with a wire brush or file before measurements are attempted. Generally, it is possible to make corrosion measurements through thin layers of rust, as long as the rust is smooth and well bonded to the metal below. Some very rough cast or corroded surfaces may have to be filed or sanded smooth in order to ensure proper sound coupling. It may also be necessary to remove paint if it has been applied in thick coats, or if it is flaking off the metal. While it is often possible to make standard corrosion measurements through thin coats of paint (on the order of a few thousandths of an inch or 0.1–0.2 mm), thick paint will attenuate signals or possibly create false echoes and requires special techniques such as echo-to-echo or THRU-COAT® measurement. Severe pitting on the outside surface of a pipe or tank can be a problem. On some rough surfaces, the use of a gel or grease rather than a liquid couplant will help transmit sound energy into the test piece. In extreme cases, it will be necessary to file or grind the surface sufficiently flat to permit contact with the face of the transducer. In applications where deep pitting occurs on the outside of a pipe or tank, it is usually necessary to measure remaining metal thickness from the base of the pits to the inside wall. There are sophisticated ultrasonic techniques utilizing focused immersion transducers that can measure directly from the base of an external pit to the inside wall, but this is generally not practical for field work. The conventional technique is to measure unpitted metal thickness ultrasonically, measure pit depth mechanically, and subtract the pit depth from the measured wall thickness. Alternatively, one can file or grind the surface down to the base of the pits and measure normally. As with any difficult application, experimentation with actual part samples is the best way to determine the limits of a particular gage/transducer combination on a given surface.

3. Transducer Positioning/Alignment:

For proper sound coupling, the transducer must be pressed firmly against the test surface. On small-diameter cylindrical surfaces, such as pipes, hold the transducer so that the sound barrier material visible on the probe face is aligned perpendicular to the center axis of the pipe (see the illustration below). While firm hand pressure on the transducer is necessary for good readings, the probe should never be scraped along or twisted against a rough metal surface. This will scratch the face of the transducer and eventually degrade performance. The safest technique for moving a transducer along a rough surface is to pick it up and reposition it for each measurement, not to slide it along. Remember that an ultrasonic test measures thickness at only one point within the beam of the transducer, and that, in corrosion situations, wall thicknesses often vary considerably. Test procedures usually call for making a number of measurements within a defined area and establishing a minimum and/or average thickness. Ideally, data should be taken at increments no greater than half the diameter of the transducer to help ensure that no pits or other local variations in wall thickness are missed. It is up to the user to define a pattern of data collection appropriate to the needs of a given application. It is possible that on some severely corroded or pitted materials there will be spots where readings cannot be obtained. This can happen when the inside surface of the material is so irregular that the sound energy is scattered rather than being reflected back to the transducer. Lack of a reading may also indicate a thickness outside the range of the transducer and instrument being used. Generally, an inability to obtain a valid thickness reading at a particular point on a test specimen could be a sign of a seriously degraded wall, which may warrant investigation by other means.

probe position

4. High temperature Measurements:

Corrosion measurements at elevated temperatures require special consideration. Keep in mind the following points:

  • Be sure that the surface temperature of the test piece does not exceed the maximum specified temperature for the transducer and couplant that you are using. Some duals are designed for room temperature measurements only.
  • Use a couplant rated for the temperature where you will be working. All high temperature couplants will boil off at some temperature, leaving a hard residue that is not able to transmit sound energy. Maximum recommended temperatures for our couplants are as follows:
     

    Part Number

    Description

    Volume

    Application

    B2

    Glycerin

    2 oz. (0.06 liter)

    General purpose, more viscous, and has a high acoustic impedance, making it a preferred couplant for rough surfaces. For ambient temperature use.

    D12

    Gel Type

    12 oz. (0.35 liter)

    For rough surfaces, overhead surfaces, or vertical walls. For ambient temperature use.

    H-2

    High Temp

    2 oz. (0.06 liter)

    Temperature range 0 °F (-18 °C) to 750 °F (400 °C) in many open environment applications when used per manufacturer's recommended procedure.*

    I-2

    High Temp

    2 oz. (0.06 liter)

    Temperature range 700–1000 °F (371–538 °C); for more details please reference the SDS.*

    *Typical UT flaw and thickness applications use thin couplant films in an open environment where the small amount of gas formed can dissipate quickly. However, if an unlikely couplant gas auto ignition flash is of major concern, this couplant should not be used above the auto ignition temperature provided on the SDS.

  • Make measurements quickly and allow the transducer body to cool between reading. High temperature duals have delay lines made of thermally tolerant material, but with continuous exposure to very high temperatures the inside of the probe will heat to a point where bonds will fail, destroying the transducer. The instrument's freeze function is useful for capturing a reading during tests that require brief surface contact.
  • Remember that both material sound velocity and transducer zero offset will change with temperature. For maximum accuracy at high temperatures, velocity calibration should be performed using a section of the test bar of known thickness heated to the temperature where measurements are to be performed. Alternately, advanced gages such as the 38DL PLUS provide software that can be programmed to automatically compensate velocity for known temperature variations. All Olympus corrosion gages have a semi-automatic zero function that can be employed to adjust zero setting at high temperatures. See the instrument operating manual for details. For other gages and flaw detectors, see their operating manual for information on how to compensate for zero drift at elevated temperatures. Additionally, it is frequently necessary to increase gain when measuring at elevated temperatures. All Olympus corrosion gages have either continuous gain adjustment or a gain boost function that can be used for this purpose.

5. Gages and Flaw Detectors:

An ultrasonic corrosion gage is designed to detect and measure echoes reflected from the inside wall of a test piece. It is possible that material discontinuities such as flaws, cracks, voids, or laminations may produce echoes of sufficient amplitude to trigger the gage, showing up as unusually thin measurements at particular spots on a test piece. However, a corrosion gage is not designed for flaw or crack detection and cannot be relied upon to detect material discontinuities. A proper evaluation of material discontinuities requires an ultrasonic flaw detector, such as the Olympus EPOCH 6LT or EPOCH 650 instruments, used by a properly trained operator. In general, any unexplained readings by a corrosion gage merit further examination.

Olympus IMS

이 애플리케이션에 사용되는 제품
EPOCH 6LT 휴대용 초음파 결함 탐상기는 한 손 작업에 최적화되어 있으며 로프 접근 및 고소 작업이 필요한 고휴대성 응용 분야에서 탁월한 성능을 제공합니다. 가볍고 인체 공학적 디자인으로 사용자의 손에 단단히 고정시키나 로프 접근이 필요한 응용 분야에서는 다리에 묶을 수 있습니다.
초음파 탐촉자는 결함 감지, 두께 측정, 소재 연구 및 의료 진단과 같은 다양한 응용 분야에 사용됩니다. 5000개 이상의 초음파 탐촉자 유형은 다양한 스타일, 요소 직경, 주파수 및 커넥터 스타일로 제공됩니다.
EPOCH 650은 다양한 응용 분야에 대한 우수한 검사 성능과 유용성을 갖춘 재래식 초음파 결함 검출기입니다. 이 직관적이고 견고한 장비는 인기 있는 EPOCH 600 결함 탐상기 후속작이며 추가 기능을 갖추고 있습니다.
45MG 고급 초음파 두께 측정기에는 표준 측정 기능은 물론 다양한 소프트웨어 옵션이 있습니다.이 독특한 두께 측정 도구는 당사의 이중 요소 및 단일 요소 두께 측정 탐촉자와 호환됩니다.

다용도로 활용 가능한 38DL PLUS™ 측정기를 이중 요소 탐촉자와 함께 사용하면 부식된 파이프의 두께를 측정할 수 있으며, 단일 요소 탐촉자를 사용하면 박층 또는 다층 소재의 두께를 매우 정확하게 측정할 수 있습니다.

27MG 기본 초음파 두께 측정기는 내부가 부식되거나 침식된 금속 파이프 및 부품의 한쪽에서 두께를 정확하게 측정할 수 있도록 설계되었습니다.이 제품은 가볍고 내구성이 있으며, 한 손으로 손쉽게 조작할 수 있도록 인체공학적으로 설계되었습니다.
죄송합니다. 이 페이지는 해당 국가에서 사용할 수 없습니다.
아래 양식을 작성하여 원하는 내용을 알려주십시오.
죄송합니다. 이 페이지는 해당 국가에서 사용할 수 없습니다.